Dissovlving Magnesium alloy from High Broad Co.

September 6, 2017

hakkında en son şirket haberleri Dissovlving Magnesium alloy from High Broad Co.

Dissovlving Magnesium alloy from High Broad Co.

 

A biodegradable material widely used in the field of oil extraction, underground tools sealed ball material, the use of soluble magnesium alloy manufacturing fracturing construction tools, tools in the work after the completion of their own work in the underground ablation, and then mixed in the liquid through the pipeline anti-discharge , Can be completely degraded, there is no easy card astringent, blocking the channel problem, thus eliminating the need for drilling recovery process, reduce the project difficulty, improve the construction efficiency

 

Product mechanical properties

 

1.Tensile strength: > 135MPa,

yield strength: > 100 MPa,

elongation: > 0.5%,

Brinell hardness: > 70HBW.

Corrosion rate: material in 3% potassium chloride solution, Constant temperature of 92 centidegrees After 24 hours of corrosion, 8-18 mg / cm2.h.

 

2.Tensile strength: > 180MPa;

yield strength: > 80 MPa;

elongation: > 8%,

Brinell hardness: > 50HBW;

corrosion rate: material in 3% potassium chloride solution, constant temperature 92 centidegrees , After 24 hours of corrosion:6-16 mg / cm2.h

 

3.Tensile strength:> 260MPa;

yield strength: > 200 MPa;

elongation: > 8%,

Brinell hardness: > 70HBW;

corrosion rate: the material in 3% potassium chloride solution, constant temperature 92 centidegree, After 24 hours of corrosion :20-40 mg / cm2.h.