Pressureless Sintered Silicon Carbide Ceramic Tile NIJ Level III Ballistic Plate 100x100x8mm
Ürün ayrıntıları:
| Menşe yeri: | Hunan, Çin |
| Marka adı: | HB |
| Sertifika: | ISO 9001:2015, NIJ 0101.06 |
| Model numarası: | aynen fayans |
| Belge: | SIC Ballistic Armor Tiles-P...ad.pdf |
Ödeme & teslimat koşulları:
| Min sipariş miktarı: | 1000 Adet |
|---|---|
| Fiyat: | USD 0.1-1 / Piece |
| Ambalaj bilgileri: | EPE köpük ara katmanı + nem bariyerli ihracat sınıfı kontrplak kutu |
| Teslim süresi: | Stok için 5-7 iş günü, üretim için 15-20 gün |
| Ödeme koşulları: | T/T,L/C,Western Union |
| Yetenek temini: | Aylık 3000000 adet |
|
Detay Bilgi |
|||
| Eğilme Dayanımı: | 380-450MPa | Döşeme Boyutu: | 100x100mm |
|---|---|---|---|
| Alan Yoğunluğu: | ≤36 kg/m² | Kırılma Tokluğu: | 3,5-4,5 MPa·m½ |
| Kalınlık: | 8.0mm | Yoğunluk: | 3,10-3,15 g/cm³ |
| Vurgulamak: | Pressureless Sintered SiC Ceramic,Cost Effective Ballistic Tile,NIJ III Strike Face Plate |
||
Ürün Açıklaması
Pressureless Sintered Silicon Carbide Ceramic Strike Face Tile NIJ Level III Ballistic Plate 100x100x8mm
Pressureless Sintered Silicon Carbide Ceramic Strike Face Tile
NIJ Level III Ballistic Protection | Cost-Effective Alternative to Boron Carbide | Superior Multi-Hit Performance
Product Introduction
The HB SIC Tile is a pressureless (atmospheric) sintered silicon carbide ceramic strike face tile engineered for NIJ Level III ballistic protection systems. Compared with conventional hot-pressed boron carbide (B4C) tiles, our atmospheric sintering process significantly reduces manufacturing costs while delivering comparable hardness (2500-2800 HV) and excellent multi-hit capability. When benchmarked against alumina (Al2O3) strike faces, the SiC tile offers 15-20% lower areal density, enabling lighter armor configurations without compromising protection levels.
Material Comparison: SiC vs B4C vs Al2O3
| Property | SiC (WNRLN) | Boron Carbide (B4C) | Alumina (Al2O3) |
|---|---|---|---|
| Density (g/cm³) | 3.10 - 3.15 | 2.50 - 2.52 | 3.70 - 3.90 |
| Hardness (HV) | 2500 - 2800 | 2800 - 3200 | 1400 - 1800 |
| Flexural Strength (MPa) | 380 - 450 | 300 - 400 | 300 - 380 |
| Fracture Toughness (MPa*m½) | 3.5 - 4.5 | 2.5 - 3.5 | 3.5 - 4.0 |
| Cost Factor | ★★ (Moderate) | ★★★★ (High) | ★ (Low) |
| Weight Efficiency | ★★★★☆ | ★★★★★ | ★★★☆☆ |
HB atmospheric sintered SiC delivers the optimal balance of performance and cost.
Key Advantages
- Cost Advantage vs Boron Carbide: Atmospheric pressure sintering eliminates the need for expensive hot-press equipment, reducing production costs by 40-60% compared to B4C while retaining 85-90% of its ballistic performance.
- Weight Advantage vs Alumina: With a density of only 3.10 g/cm³, SiC is 15-20% lighter than alumina (3.70-3.90 g/cm³), allowing armor designers to achieve equivalent protection at significantly reduced weight.
- Superior Multi-Hit Capability: Higher fracture toughness (3.5-4.5 MPa*m½) compared to B4C ensures better crack resistance and multi-hit performance, maintaining protection integrity after initial impact.
- Flexible Sizing & Customization: Available in standard 100x100mm tiles with custom dimensions up to 150x150mm. Thickness ranging from 6mm to 12mm to meet different protection level requirements.
Technical Specifications
Material Grade
SiC (Pressureless Sintered)
Density
3.10 - 3.15 g/cm³
Hardness (Vickers)
2500 - 2800 HV
Flexural Strength
380 - 450 MPa
Fracture Toughness
3.5 - 4.5 MPa*m½
Areal Density @ 8mm
≤ 36 kg/m²
Standard Dimensions
100 x 100 mm
Standard Thickness
8.0 mm (2-12mm available)
Applications
Why Choose HB SiC Strike Face Tiles?
- In-House Sintering: Complete manufacturing control from powder to finished tile
- Batch Traceability: Every tile is lot-coded with full material certification
- Flexible MOQ: Starting from 50 pieces for trial orders
- Global Logistics: Secure export packaging with full customs documentation
Request your technical datasheet and quotation today
Email: janehu@hbnewmaterial.com
Custom dimensions and thickness available upon request